We can produce the following models for your choice
1000 Series：1A99,1A97,1A95,1A93,1A90,1A85,1080,1080A,1070,1070A,1370,1060,1050,1350,1145,1035,1A30,1100,1200,1235,
2000 Series：2A01,2A02,2A04,2A06,2A10,2A11,2B11,2A12,2B12,2A13,2A14,2A16,2B16,2A17,2A20,2A21,2A25,2A49,2A50,
2B50,2A70,2B70,2A80,2A90,2004,2011,2014,2014A,2214,2017,2017A,2117,2218,2618,2219,2024,2124
3000 Series：3A21,3003,3103,3004,3005,3105
4000 Series：4A01,4A11,4A13,4A17,4004,4032,4043,4043A,4047,4047A
5000 Series：5A01,5A02,5A03,5A05,5B05,5A06,5B06,5A12,5A13,5A30,5A33,5A41,5A43,5A66,5005,5019,5050,5251,5052,
5154,5154A, 5454,5554,5754,5056,5356,5456,5082,5182,5083,5086
6000 Series：6A02,6B02,6A51,6101,6101A,6005,6005A,6351,6060,6061,6063,6063A,6070,6181,6082
7000 Series：7A01,7A03,7A04,7A05,7A09,7A10,7A15,7A19,7A31,7A33,7A52,7003,7005,7020,7022,7050,7075,7475
8000 Series：8A06,8011,8090
Temper：O,H12,H13,H14,H16,H18,H24,H32,H34,H19,H38,G36,F,H111,H112,H192,H392,H393,H321
T1,T3,T4,T8,T72,T451,T42,T62,T5,T6,T36,T351,T651,T851,T3511,T913,T94,T7351,T89,T4510,T6510,T8510,T8511,T4511,T52,T5511,T6511,T54,T73
| NO | Features & requirements | Test items | Test methods | Reguirements |
| 1 | Coating thickness | Thickness | Chambre captivity | (Single side)(0.001mm-0.002mm) |
| 2 | Adgesiive power | Adhesion test | Blade grid maker | Coat not fall off |
| Cupping test | Cupping machine | Coat not fall off | ||
| bend test | Vise | Coat not fall off | ||
| 3 | hydrophilic(initial stage) | Contact angle | Drip contact |
≤10° ≥2.5mm ≤10° ≥2.5mm |
| After washing | Drip contact |
≤15° ≥2.5mm ≤15° ≥2.5mm |
||
| Water drop test |
≥3.0mm ≥3.0mm |
|||
| 4 |
(continuance)hydrophilic |
Dead water dipping test | Dry and met cycle tank |
≤30° ≥2.5mm ≤30° ≥2.5mm |
| Dry and wet cycle test |
≤35° ≥2.5mm ≤35° ≥2.5mm |
|||
| 5 | Corrosion | Salt.spray test | (72h)Salt.spray tester |
≥tNo9.8no hole |
| 6 | Heat-resisting Property | 200°C | Heat 5°C min in the oven at 200°C |
No color change No terrible smell |
| 7 | Solvent Resistance | Heat and dissolve trethylene | ≤1% | |
| 8 | Alkaline Resistance | The change of hydrophilicity after alkali eroding | ≥2.5mm | |
| 9 | Anti-volatility | Naphtha's effect on coat's hydrophilicity | ≥2.5mm | |
| 10 | Trethylene-resistant | trethylene's on coat's hydrophilicity | ≥2.5mm | |
Chemical Composition%
|
No. |
Alloy |
Si |
Fe |
Cu |
Mn |
Mg |
Cr |
Ni |
Zn |
Ti |
Zr |
Others |
Al |
|
|
Each |
Total |
|||||||||||||
|
1 |
8011 |
0.50-0.9 |
0.6-1.0 |
0.1 |
0.2 |
0.05 |
0.05 |
— |
0.1 |
0.08 |
— |
0.05 |
0.15 |
Remain |